论文题目: Synthesis of Ag/BiVO4/rGO composite with enhanced photocatalytic degradation of triclosan
英文论文题目: Synthesis of Ag/BiVO4/rGO composite with enhanced photocatalytic degradation of triclosan
第一作者: Li, M.
英文第一作者: Li, M.
联系作者: 于泳
英文联系作者: Yu Yong
外单位作者单位:
英文外单位作者单位:
发表年度: 2019
卷: 664
期:
页码: 230-239
摘要:

A ternary visible-light driven photocatalyst, Ag/BiVO4/reduced graphene oxide (rGO) composite was manufactured by hydrothermal strategy. The optimized products were characterized by XRD, SEM, HRTEM, EDS, XPS, DRS, Raman spectra, PL, BET, photocurrent density and EIS analysis. Compared to pure BiVO4, the fabricated ternary composite showed enhanced photocatalytic ability to decompose pollutant under visible light. Triclosan was completely removed after 100min in solution with 1mg/mL photocatalyst under visible light irradiation. Repeated cycle tests demonstrated the photo-stability and reusability of composite to decompose triclosan, indicating that this material could be utilized repeatedly. The upgraded photocatalytic ability was attributed to the addition of Ag and rGO, which enhanced the charge separation and inhibited the recombination of photogenerated electrons and holes. The EPR spin-trap technique (with DMPO) was performed to identify the radicals produced in Ag/BiVO4/rGO under the visible light, and trapping experiments were conducted to determine the main active species in the photocatalytic process of decomposing triclosan. Finally, seven reaction intermediates of triclosan were detected by LC-MS/MS and possible degradation routes were proposed. 

英文摘要:

A ternary visible-light driven photocatalyst, Ag/BiVO4/reduced graphene oxide (rGO) composite was manufactured by hydrothermal strategy. The optimized products were characterized by XRD, SEM, HRTEM, EDS, XPS, DRS, Raman spectra, PL, BET, photocurrent density and EIS analysis. Compared to pure BiVO4, the fabricated ternary composite showed enhanced photocatalytic ability to decompose pollutant under visible light. Triclosan was completely removed after 100min in solution with 1mg/mL photocatalyst under visible light irradiation. Repeated cycle tests demonstrated the photo-stability and reusability of composite to decompose triclosan, indicating that this material could be utilized repeatedly. The upgraded photocatalytic ability was attributed to the addition of Ag and rGO, which enhanced the charge separation and inhibited the recombination of photogenerated electrons and holes. The EPR spin-trap technique (with DMPO) was performed to identify the radicals produced in Ag/BiVO4/rGO under the visible light, and trapping experiments were conducted to determine the main active species in the photocatalytic process of decomposing triclosan. Finally, seven reaction intermediates of triclosan were detected by LC-MS/MS and possible degradation routes were proposed. 

刊物名称: Science of the Total Environment
英文刊物名称: Science of the Total Environment
论文全文:
英文论文全文:
全文链接:
其它备注:
英文其它备注:
学科:
英文学科:
影响因子:
第一作者所在部门:
英文第一作者所在部门:
论文出处:
英文论文出处:
论文类别:
英文论文类别:
参与作者: M. Li, G. H. Xu, Z. Y. Guan, Y. Wang, H. W. Yu and Y. Yu
英文参与作者: M. Li, G. H. Xu, Z. Y. Guan, Y. Wang, H. W. Yu and Y. Yu